HB-YD165(Q)高硬度耐磨焊丝厂家
hb-yd165(q)高硬度耐磨焊丝厂家
hb-yd165(q) 高硬度耐磨焊丝hb-yd165(q) 高硬度堆焊焊丝
hb-yd114(q)
1.6
50-55
(受强烈冲击后
after high impact)
钢堆焊焊丝，受强烈冲击后，表面具有加工硬度的特点。
high-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
hb-yd115(q)
1.6
50-55
(受强烈冲击后after high impact)
用于受严重冲击钢堆焊，加工硬化效果显著。
applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
hb-yd165(q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
high hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
hb-yd172(q)
1.6
≥40
用于堆焊齿轮、挖泥斗、矿山机械等磨损件
applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.
hb-yd207(q)
1.6
≥50
用于堆焊推土机刀片，螺旋桨等磨损零件
applied to repair surface of high wear parts, such as bulldozer blade and propeller.
hb-yd212(q)
1.2/1.6
≥50
用于堆焊各种受磨损的机件表面，如齿轮、挖斗、矿山机械
applied to repair surface of wear parts, such as gear mud bucket and mining machinery.
hb-yd256(q)
1.6
hb≥170
钢堆焊，适用于破碎机等受冲击磨损部位的堆焊
high-manganese steelhardfacing flux-cored wires,it is applied to repair surface of high impact wear parts, such as crusher.
hb-yd258(q)
1.6
55-60
用于耐磨表面堆焊
applied to repair surface of wear parts.
hb-yd265(q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
high hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
hb-yd322(q)
1.6
≥55
用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件
applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.
hb-yd327a(q)
1.6
≥55
专门用于模具堆焊，耐磨性能高于d322
used tomouldsurfacing, wear resistance is better than d322.
hb-yd337(q)
1.6
≥48
用于铸钢或锻钢上堆焊锻模
applied to repairforging dieatcast steelorforging steel.
hb-yd397(q)
1.6
≥40
用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件
applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing.
hb-yd405a(q)
1.6
50-59
用于热轧辊开坯辊堆焊
applied to repair hot-rolling blooming rollor.
hb-yd430a(q)
1.6
20-35
打底层堆焊焊丝
a backing hardfacing flux-cored wires
hb-yd488a(q)
1.6
45-50
用于轧辊堆焊
applied to repair rollor
hb-yd507mo(q)
1.6
35-45
用于510℃以下中高压阀门堆焊
applied to valve which operating tdivperature is less than 510℃.
hb-yd518(q)
1.6
40-50
用于连铸辊堆焊
applied to repaircontinuous caster roller
hb-yd688(q)
1.6
50-60
用于磨煤辊打底焊(韧性好，可以多层堆焊)
used to coal roller backing welding.
hb-yd788(q)
1.6
55-62
硬度高，可以多层堆焊。
high hardness andmulti-layer welding
hb-yd888(q)
1.2, 1.6
60-65
硬度高，堆焊层厚度不超过6mm。
high hardness, but thethicknessofsurfacing layeris less than 6mm.
hb-yd165(q) 高硬度耐磨焊丝
广泛应用于矿渣破碎机易损件（如破碎机锤头、锤盘、反击板），水泥立窑卸料装置（塔盘、塔尖、塔篦），制砖机(绞刀、搅拌机叶片、搅笼、对辊、锤破、笼破、挖泥机叶片),发电厂风机叶片，炼钢厂(高炉溜槽衬板，对辊，圆锥破),破碎机、锤头、挤压辊、搅拌机叶片,木炭机,铣鞋、磨鞋、扶***、扩孔器、钻杆接头、水力割刀、刮刀片、刨煤机刨刀、取芯钻头、打桩钻头、螺旋钻头、钻头修补,路政机械合金拌刀;路政机械开沟机合金刀头刀库;起爆机合金顶头等。为采（选）矿、造船、电力、石化、冶金、食品、纺织、机制炭、供水、塑料、陶瓷、玻璃、模具、建材、航天、海洋工程、船舶等行业的易磨损件的修补，
、
详细描述
1、d908型耐热耐蚀耐磨堆焊条
熔敷金属化学成分(%)
c mn si cr w ni b4c mo v 其它
≤1.0 ≤2.0 ≤1.5 10.0-15.0 1.0-2.0 1.0-3.0 ≤1.0 1.0-3.0 ≤1.0 ≤4.0
焊层硬度hrc≥60 耐热温度≤600℃ 可堆焊铸铁碳钢、合金钢、不锈钢等母材，抗裂性好，交直流两用，冷焊.
2、d918型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w b4c mo v 其它
1.0-3.0 ≤2.0 ≤1.0 20.0-30.0 2.0-3.0 ≤2.0 ≤2.0 ≤1.0 ≤4.0
焊层硬度hrc-70 耐热温度≤600℃ 可堆焊铸铁碳钢、合金钢、不锈钢等母材，交直流两用，母材预热、焊后缓冷.
3、d910型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni mo v 其它
≤1.0 ≤1.50 ≤1.0 5.0-10.0 1.0-2.0 ≤1.0 ≤2.0 ≤0.5 ≤4.0
焊层硬度hrc≥55 耐热温度≤500℃ 可堆焊各种金属母材、合金钢，交直流两用，抗裂性好.直接冷焊.
4、d928型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni co mo v 其它
≤1.5 ≤2.0 ≤1.5 25.0-35.0 4.0-6.0 ≤5.0 ≤5.0 ≤3.0 ≤1.50 ≤4.0
焊层硬度hrc≥60-70 耐热温度≤800℃ 可堆焊各种金属母材,交直流两用，抗裂性好.直接冷焊.
5、d912型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w mo v 其它
≤0.5 ≤1.50 ≤1.0 5.0-10.0 ≤1.0 1.0 ≤0.5 ≤4.0
焊层硬度hrc≥45 耐热温度≤600℃ 可堆焊碳钢、合金钢，不锈钢等母材，抗裂性好,交直流两用.
6、d938型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni mo v 其它
≤1.0 10.0-15.0 ≤1.5 10.0-15.0 2.0-4.0 1.50-3.0 1.0-2.0 ≤1.0 ≤4.0
焊层硬度hrc28-40 耐热温度≤800℃ 可堆焊碳钢、合金钢，不锈钢等母材，系钢厂吊车、热剪口专用焊条，也可用于其它冷热交替磨损零部件的恢复堆焊。交直流两用，直接冷焊。
7、d947型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni co mo v nb
≤0.50 ≤1.50 ≤1.5 余量 3.0-5.0 20.0-30.0 ≤5.0 10.0-20.0 ≤1.0 ≤2.0
焊层硬度hrc25-40 耐热温度≤1000℃ 可堆焊碳钢、合金钢，不锈钢等母材，可应用于进口锻床、锤头等。高温高冲击零部件
手机访问更方便 扫一扫手机查看 微官网和产品信息
济南晶鼎焊接材料有限公司
18678398141
qq: 1345905480
TM-V211乙烯基酯树脂
通州办理三类医疗器械许可证没有实际办公地址可以吗
100篇10万+爆文标题，看了再也不担心自己写不好标题了
番禺小别墅设计怎么样，色彩所代表的形象风格
供应模具钢DC53 规格齐全 欢迎咨询
HB-YD165(Q)高硬度耐磨焊丝厂家
浙江墨瑟铝木门窗代理，铝木复合门窗价格上指寻 质优价廉.
电镀白酒瓶厂家介绍白酒几乎都采用玻璃瓶包装的真正原因
冰果漫吸奶茶 吸引消费者的味蕾
企事业单位厨房设计、厨房、诚兴厨业(在线咨询)
双流区月子会所坐月子一个月多少钱
墨丁文化传媒(在线咨询)、雅思、昆山雅思阅读机构
新一代物联网技术在消防行业中的创新应用——乐鸟
水泥砂浆防腐钢管经典成就未来-诚源管业
开一家头疗馆需要多少钱？有费用低的大型加盟品牌吗？
为什么越来越多的家庭选择系统门窗，原因让人意想不到
基隆玻璃纤维筋施工指导
广州悦洋中学生出国游学中介墨尔本悉尼双城夏令营火热报名中
宁夏高档酒店查看 ，贺兰山宴会中心在哪了呢？
通州区武夷花园显示器回收哪家正规
hb-yd165(q) 高硬度耐磨焊丝hb-yd165(q) 高硬度堆焊焊丝
hb-yd114(q)
1.6
50-55
(受强烈冲击后
after high impact)
钢堆焊焊丝，受强烈冲击后，表面具有加工硬度的特点。
high-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
hb-yd115(q)
1.6
50-55
(受强烈冲击后after high impact)
用于受严重冲击钢堆焊，加工硬化效果显著。
applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
hb-yd165(q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
high hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
hb-yd172(q)
1.6
≥40
用于堆焊齿轮、挖泥斗、矿山机械等磨损件
applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.
hb-yd207(q)
1.6
≥50
用于堆焊推土机刀片，螺旋桨等磨损零件
applied to repair surface of high wear parts, such as bulldozer blade and propeller.
hb-yd212(q)
1.2/1.6
≥50
用于堆焊各种受磨损的机件表面，如齿轮、挖斗、矿山机械
applied to repair surface of wear parts, such as gear mud bucket and mining machinery.
hb-yd256(q)
1.6
hb≥170
钢堆焊，适用于破碎机等受冲击磨损部位的堆焊
high-manganese steelhardfacing flux-cored wires,it is applied to repair surface of high impact wear parts, such as crusher.
hb-yd258(q)
1.6
55-60
用于耐磨表面堆焊
applied to repair surface of wear parts.
hb-yd265(q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
high hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
hb-yd322(q)
1.6
≥55
用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件
applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.
hb-yd327a(q)
1.6
≥55
专门用于模具堆焊，耐磨性能高于d322
used tomouldsurfacing, wear resistance is better than d322.
hb-yd337(q)
1.6
≥48
用于铸钢或锻钢上堆焊锻模
applied to repairforging dieatcast steelorforging steel.
hb-yd397(q)
1.6
≥40
用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件
applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing.
hb-yd405a(q)
1.6
50-59
用于热轧辊开坯辊堆焊
applied to repair hot-rolling blooming rollor.
hb-yd430a(q)
1.6
20-35
打底层堆焊焊丝
a backing hardfacing flux-cored wires
hb-yd488a(q)
1.6
45-50
用于轧辊堆焊
applied to repair rollor
hb-yd507mo(q)
1.6
35-45
用于510℃以下中高压阀门堆焊
applied to valve which operating tdivperature is less than 510℃.
hb-yd518(q)
1.6
40-50
用于连铸辊堆焊
applied to repaircontinuous caster roller
hb-yd688(q)
1.6
50-60
用于磨煤辊打底焊(韧性好，可以多层堆焊)
used to coal roller backing welding.
hb-yd788(q)
1.6
55-62
硬度高，可以多层堆焊。
high hardness andmulti-layer welding
hb-yd888(q)
1.2, 1.6
60-65
硬度高，堆焊层厚度不超过6mm。
high hardness, but thethicknessofsurfacing layeris less than 6mm.
hb-yd165(q) 高硬度耐磨焊丝
广泛应用于矿渣破碎机易损件（如破碎机锤头、锤盘、反击板），水泥立窑卸料装置（塔盘、塔尖、塔篦），制砖机(绞刀、搅拌机叶片、搅笼、对辊、锤破、笼破、挖泥机叶片),发电厂风机叶片，炼钢厂(高炉溜槽衬板，对辊，圆锥破),破碎机、锤头、挤压辊、搅拌机叶片,木炭机,铣鞋、磨鞋、扶***、扩孔器、钻杆接头、水力割刀、刮刀片、刨煤机刨刀、取芯钻头、打桩钻头、螺旋钻头、钻头修补,路政机械合金拌刀;路政机械开沟机合金刀头刀库;起爆机合金顶头等。为采（选）矿、造船、电力、石化、冶金、食品、纺织、机制炭、供水、塑料、陶瓷、玻璃、模具、建材、航天、海洋工程、船舶等行业的易磨损件的修补，
、
详细描述
1、d908型耐热耐蚀耐磨堆焊条
熔敷金属化学成分(%)
c mn si cr w ni b4c mo v 其它
≤1.0 ≤2.0 ≤1.5 10.0-15.0 1.0-2.0 1.0-3.0 ≤1.0 1.0-3.0 ≤1.0 ≤4.0
焊层硬度hrc≥60 耐热温度≤600℃ 可堆焊铸铁碳钢、合金钢、不锈钢等母材，抗裂性好，交直流两用，冷焊.
2、d918型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w b4c mo v 其它
1.0-3.0 ≤2.0 ≤1.0 20.0-30.0 2.0-3.0 ≤2.0 ≤2.0 ≤1.0 ≤4.0
焊层硬度hrc-70 耐热温度≤600℃ 可堆焊铸铁碳钢、合金钢、不锈钢等母材，交直流两用，母材预热、焊后缓冷.
3、d910型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni mo v 其它
≤1.0 ≤1.50 ≤1.0 5.0-10.0 1.0-2.0 ≤1.0 ≤2.0 ≤0.5 ≤4.0
焊层硬度hrc≥55 耐热温度≤500℃ 可堆焊各种金属母材、合金钢，交直流两用，抗裂性好.直接冷焊.
4、d928型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni co mo v 其它
≤1.5 ≤2.0 ≤1.5 25.0-35.0 4.0-6.0 ≤5.0 ≤5.0 ≤3.0 ≤1.50 ≤4.0
焊层硬度hrc≥60-70 耐热温度≤800℃ 可堆焊各种金属母材,交直流两用，抗裂性好.直接冷焊.
5、d912型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w mo v 其它
≤0.5 ≤1.50 ≤1.0 5.0-10.0 ≤1.0 1.0 ≤0.5 ≤4.0
焊层硬度hrc≥45 耐热温度≤600℃ 可堆焊碳钢、合金钢，不锈钢等母材，抗裂性好,交直流两用.
6、d938型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni mo v 其它
≤1.0 10.0-15.0 ≤1.5 10.0-15.0 2.0-4.0 1.50-3.0 1.0-2.0 ≤1.0 ≤4.0
焊层硬度hrc28-40 耐热温度≤800℃ 可堆焊碳钢、合金钢，不锈钢等母材，系钢厂吊车、热剪口专用焊条，也可用于其它冷热交替磨损零部件的恢复堆焊。交直流两用，直接冷焊。
7、d947型耐磨焊条
熔敷金属化学成分(%)
c mn si cr w ni co mo v nb
≤0.50 ≤1.50 ≤1.5 余量 3.0-5.0 20.0-30.0 ≤5.0 10.0-20.0 ≤1.0 ≤2.0
焊层硬度hrc25-40 耐热温度≤1000℃ 可堆焊碳钢、合金钢，不锈钢等母材，可应用于进口锻床、锤头等。高温高冲击零部件
手机访问更方便 扫一扫手机查看 微官网和产品信息
济南晶鼎焊接材料有限公司
18678398141
qq: 1345905480
TM-V211乙烯基酯树脂
通州办理三类医疗器械许可证没有实际办公地址可以吗
100篇10万+爆文标题，看了再也不担心自己写不好标题了
番禺小别墅设计怎么样，色彩所代表的形象风格
供应模具钢DC53 规格齐全 欢迎咨询
HB-YD165(Q)高硬度耐磨焊丝厂家
浙江墨瑟铝木门窗代理，铝木复合门窗价格上指寻 质优价廉.
电镀白酒瓶厂家介绍白酒几乎都采用玻璃瓶包装的真正原因
冰果漫吸奶茶 吸引消费者的味蕾
企事业单位厨房设计、厨房、诚兴厨业(在线咨询)
双流区月子会所坐月子一个月多少钱
墨丁文化传媒(在线咨询)、雅思、昆山雅思阅读机构
新一代物联网技术在消防行业中的创新应用——乐鸟
水泥砂浆防腐钢管经典成就未来-诚源管业
开一家头疗馆需要多少钱？有费用低的大型加盟品牌吗？
为什么越来越多的家庭选择系统门窗，原因让人意想不到
基隆玻璃纤维筋施工指导
广州悦洋中学生出国游学中介墨尔本悉尼双城夏令营火热报名中
宁夏高档酒店查看 ，贺兰山宴会中心在哪了呢？
通州区武夷花园显示器回收哪家正规